- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.929
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 6.5 % | 6.5 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.55 g/10 min | 0.55 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Dart Drop | 18.9 g/micron | 480 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 25.5 MPa | 3700 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 103 MPa | 15000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 110 MPa | 16000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.8 % | 4.8 % | ASTM D1003 | ||
| Gloss | 74 % | 74 % | at 45º; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.