- 熔体流动速率 [g/10min]: 1.25
- 密度 [g/cm3]: 0.929
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 4.7 % | 4.7 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 1.25 g/10 min | 1.25 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 | ||
| Dart Drop | 9.84 g/micron | 250 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 145 MPa | 21000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 179 MPa | 26000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D1003 | ||
| Gloss | 63 % | 63 % | at 45º; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.