- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.933
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | D1505 | ||
| Vinyl Acetate Content | 12 % | 12 % | |||
| Thickness | 33.0 microns | 1.30 mil | Thickness Tested | ||
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 300 % | 300 % | D882 | ||
| Film Elongation at Break, TD | 800 % | 800 % | D882 | ||
| Dart Drop | 7.27 g/micron | 185 g/mil | D1709 | ||
| Dart drop Test | 240 g | 0.529 lb | D1709 | ||
| Film Tensile Strength at Break, MD | 26.9 MPa | 3900 psi | D638 | ||
| Film Tensile Strength at Break, TD | 22.1 MPa | 3210 psi | D638 | ||
| 1% Secant Modulus, MD | 72.4 MPa | 10500 psi | D882 | ||
| 1% Secant Modulus, TD | 79.3 MPa | 11500 psi | D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 94.0 °C | 201 °F | DSC Peak; D3418 | ||
| Vicat Softening Point | 70.0 °C | 158 °F | D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.3 % | 2.3 % | D1003 | ||
| Gloss | 84 % | 84 % | at 45°; D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | <= 193 °C | <= 379 °F | Blown Film | ||
| <= 210 °C | <= 410 °F | Cast Film | |||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | As Tested | ||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||