- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | with antiblock; ASTM D1505 | ||
| Vinyl Acetate Content | 6.5 % | 6.5 % | |||
| Thickness | 38.1 microns | 1.50 mil | as tested | ||
| Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Dart Drop | 7.09 g/micron | 180 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.8 MPa | 3300 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 96.5 MPa | 14000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 103 MPa | 15000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 103 °C | 217 °F | Peak DSC; Westlake Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 10 % | 10 % | with 9000 ppm antiblock; ASTM D1003 | ||
| Gloss | 60 % | 60 % | at 45º (with 9000 ppm antiblock); ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 193 - 204 °C | 380 - 400 °F | |||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | as tested | ||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||