- 熔体流动速率 [g/10min]: 0.112
- 密度 [g/cm3]: 0.7
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.118
- 拉伸强度 [MPa]: 25.0
- 断裂伸长率 [%]: 33.1
- 弯曲强度 [MPa]: 19.3
- 弯曲模量 [MPa]: 1.17
- 硬度: 69.0
- 热变形温度 [℃]: 60.0
- 透光率 [%]: 74.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.700 - 1.25 g/cc | 0.0253 - 0.0452 lb/in³ | Average value: 1.17 g/cc Grade Count:251 |
| Water Absorption | 0.300 - 2.00 % | 0.300 - 2.00 % | Average value: 0.461 % Grade Count:96 |
| Moisture Absorption at Equilibrium | 0.300 - 0.600 % | 0.300 - 0.600 % | Average value: 0.399 % Grade Count:29 |
| Water Absorption at Saturation | 0.300 - 2.20 % | 0.300 - 2.20 % | Average value: 1.23 % Grade Count:21 |
| Linear Mold Shrinkage | 0.00200 - 0.00800 cm/cm | 0.00200 - 0.00800 in/in | Average value: 0.00455 cm/cm Grade Count:174 |
| Melt Flow | 0.112 - 40.0 g/10 min | 0.112 - 40.0 g/10 min | Average value: 8.51 g/10 min Grade Count:239 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 40.0 - 54.0 | 40.0 - 54.0 | Average value: 46.0 Grade Count:3 |
| Hardness, Rockwell M | 18.0 - 99.0 | 18.0 - 99.0 | Average value: 81.9 Grade Count:99 |
| Hardness, Rockwell R | 69.0 | 69.0 | Average value: 69.0 Grade Count:4 |
| Ball Indentation Hardness | 170 - 190 MPa | 24700 - 27600 psi | Average value: 179 MPa Grade Count:21 |
| Tensile Strength, Ultimate | 19.3 - 85.0 MPa | 2800 - 12300 psi | Average value: 64.0 MPa Grade Count:200 |
| Tensile Strength, Yield | 25.0 - 85.0 MPa | 3630 - 12300 psi | Average value: 59.9 MPa Grade Count:52 |
| Elongation at Break | 1.00 - 350 % | 1.00 - 350 % | Average value: 11.7 % Grade Count:242 |
| Elongation at Yield | 2.00 - 6.00 % | 2.00 - 6.00 % | Average value: 4.54 % Grade Count:58 |
| Modulus of Elasticity | 0.950 - 3.79 GPa | 138 - 550 ksi | Average value: 2.88 GPa Grade Count:193 |
| Flexural Yield Strength | 33.1 - 143 MPa | 4800 - 20700 psi | Average value: 100 MPa Grade Count:198 |
| Flexural Modulus | 1.17 - 3.59 GPa | 170 - 520 ksi | Average value: 2.78 GPa Grade Count:101 |
| Compressive Yield Strength | 36.5 - 117 MPa | 5300 - 17000 psi | Average value: 102 MPa Grade Count:8 |
| Izod Impact, Notched | 0.118 - 9.61 J/cm | 0.220 - 18.0 ft-lb/in | Average value: 0.353 J/cm Grade Count:164 |
| 0.240255 - 0.37373 J/cm @Temperature 0.000 - 0.000 °C | 0.450096 - 0.70015 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.463 J/cm Grade Count:6 | |
| 0.10678 - 0.80085 J/cm @Temperature 0.000 - 0.000 °C | 0.20004 - 1.5003 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.463 J/cm Grade Count:10 | |
| 0.10678 - 0.80085 J/cm @Thickness 3.17 - 6.35 mm | 0.20004 - 1.5003 ft-lb/in @Thickness 0.125 - 0.250 in | Average value: 0.463 J/cm Grade Count:10 | |
| 0.26695 - 0.85424 J/cm @Diameter 6.35 - 6.35 mm | 0.50011 - 1.6003 ft-lb/in @Diameter 0.250 - 0.250 in | Average value: 0.463 J/cm Grade Count:6 | |
| 0.26695 - 0.85424 J/cm @Temperature 0.000 - 0.000 °C | 0.50011 - 1.6003 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.463 J/cm Grade Count:6 | |
| Izod Impact, Notched (ISO) | 1.30 - 19.0 kJ/m² | 0.619 - 9.04 ft-lb/in² | Average value: 3.13 kJ/m² Grade Count:23 |
| Charpy Impact Unnotched | 1.00 J/cm² - NB | 4.76 ft-lb/in² - NB | Average value: 2.91 J/cm² Grade Count:56 |
| Charpy Impact, Notched | 0.140 - 2.00 J/cm² | 0.666 - 9.52 ft-lb/in² | Average value: 0.508 J/cm² Grade Count:38 |
| Gardner Impact | 0.226 - 0.339 J | 0.167 - 0.250 ft-lb | Average value: 0.231 J Grade Count:92 |
| Falling Dart Impact | 2.17 - 18.6 J | 1.60 - 13.7 ft-lb | Average value: 10.7 J Grade Count:4 |
| Tensile Creep Modulus, 1 hour | 1800 - 2700 MPa | 261000 - 392000 psi | Average value: 2460 MPa Grade Count:9 |
| Tensile Creep Modulus, 1000 hours | 1200 - 1800 MPa | 174000 - 261000 psi | Average value: 1580 MPa Grade Count:10 |
| Taber Abrasion, mg/1000 Cycles | 16.5 | 16.5 | Average value: 16.5 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+9 - 1.00e+17 ohm-cm | 2.00e+9 - 1.00e+17 ohm-cm | Average value: 3.40e+15 ohm-cm Grade Count:37 |
| Surface Resistance | 8.00e+8 - 1.00e+16 ohm | 8.00e+8 - 1.00e+16 ohm | Average value: 1.09e+15 ohm Grade Count:26 |
| Static Decay | 0.0100 - 0.100 sec | 0.0100 - 0.100 sec | Average value: 0.0343 sec Grade Count:3 |
| Dielectric Constant | 2.80 - 4.00 | 2.80 - 4.00 | Average value: 3.45 Grade Count:32 |
| Dielectric Strength | 0.787 - 60.0 kV/mm | 20.0 - 1520 kV/in | Average value: 25.5 kV/mm Grade Count:39 |
| Dissipation Factor | 0.0200 - 0.190 | 0.0200 - 0.190 | Average value: 0.0488 Grade Count:34 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:16 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 150 µm/m-°C | 16.7 - 83.3 µin/in-°F | Average value: 70.2 µm/m-°C Grade Count:168 |
| 72.0 - 149.4 µm/m-°C @Temperature -17.8 - 156 °C | 40.0 - 83.00 µin/in-°F @Temperature 0.000 - 312 °F | Average value: 94.9 µm/m-°C Grade Count:26 | |
| Specific Heat Capacity | 1.46 - 1.50 J/g-°C | 0.349 - 0.359 BTU/lb-°F | Average value: 1.47 J/g-°C Grade Count:9 |
| Thermal Conductivity | 0.187 - 0.216 W/m-K | 1.30 - 1.50 BTU-in/hr-ft²-°F | Average value: 0.202 W/m-K Grade Count:15 |
| Maximum Service Temperature, Air | 50.0 - 98.0 °C | 122 - 208 °F | Average value: 83.9 °C Grade Count:68 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 109 °C | 140 - 228 °F | Average value: 96.2 °C Grade Count:62 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.7 - 106 °C | 125 - 223 °F | Average value: 89.0 °C Grade Count:212 |
| Vicat Softening Point | 58.3 - 119 °C | 137 - 246 °F | Average value: 100 °C Grade Count:231 |
| Annealing Point | 60.0 - 90.0 °C | 140 - 194 °F | Average value: 77.1 °C Grade Count:7 |
| Heat Distortion Temperature | 85.0 - 105 °C | 185 - 221 °F | Average value: 96.4 °C Grade Count:7 |
| Glass Transition Temp, Tg | 102 - 122 °C | 216 - 252 °F | Average value: 110 °C Grade Count:21 |
| Flammability, UL94 | HB | HB | Grade Count:156 |
| Oxygen Index | 18.0 % | 18.0 % | Average value: 18.0 % Grade Count:7 |
| Glow Wire Test | 650 - 700 °C | 1200 - 1290 °F | Average value: 662 °C Grade Count:30 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.38 - 1.52 | 1.38 - 1.52 | Average value: 1.49 Grade Count:107 |
| Haze | 0.400 - 98.0 % | 0.400 - 98.0 % | Average value: 7.37 % Grade Count:163 |
| Yellow Index | -7.50 - 6.50 % | -7.50 - 6.50 % | Average value: 0.758 % Grade Count:25 |
| Transmission, Visible | 74.0 - 93.0 % | 74.0 - 93.0 % | Average value: 90.5 % Grade Count:233 |
| UV Transmittance | 0.190 - 88.5 % | 0.190 - 88.5 % | Average value: 39.8 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 177 - 265 °C | 350 - 509 °F | Average value: 237 °C Grade Count:35 |
| Nozzle Temperature | 200 - 245 °C | 392 - 473 °F | Average value: 229 °C Grade Count:6 |
| Adapter Temperature | 230 - 240 °C | 446 - 464 °F | Average value: 235 °C Grade Count:4 |
| Die Temperature | 220 - 260 °C | 428 - 500 °F | Average value: 240 °C Grade Count:14 |
| Melt Temperature | 150 - 260 °C | 302 - 500 °F | Average value: 227 °C Grade Count:54 |
| Mold Temperature | 30.0 - 107 °C | 86.0 - 225 °F | Average value: 63.3 °C Grade Count:52 |
| Roll Temperature | 80.0 - 100 °C | 176 - 212 °F | Average value: 90.0 °C Grade Count:4 |
| Drying Temperature | 60.0 - 109 °C | 140 - 228 °F | Average value: 84.0 °C Grade Count:61 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.25 hour Grade Count:56 |
| Injection Pressure | 58.8 - 147 MPa | 8530 - 21300 psi | Average value: 104 MPa Grade Count:14 |
| Back Pressure | 0.276 - 0.981 MPa | 40.0 - 142 psi | Average value: 0.567 MPa Grade Count:3 |
| Screw Speed | 20.0 - 80.0 rpm | 20.0 - 80.0 rpm | Average value: 56.4 rpm Grade Count:7 |