- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.149
- 拉伸强度 [MPa]: 37.9
- 断裂伸长率 [%]: 57.0
- 弯曲模量 [MPa]: 1.86
- 硬度: 106.0
- 透光率 [%]: 63.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.19 g/cc | 0.0415 - 0.0430 lb/in³ | Average value: 1.18 g/cc Grade Count:14 |
| Water Absorption | 0.200 - 0.400 % | 0.200 - 0.400 % | Average value: 0.317 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | Average value: 0.00425 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 46.0 - 96.0 | 46.0 - 96.0 | Average value: 81.6 Grade Count:7 |
| Hardness, Rockwell R | 106 - 110 | 106 - 110 | Average value: 108 Grade Count:5 |
| Tensile Strength, Yield | 37.9 - 72.0 MPa | 5500 - 10400 psi | Average value: 55.2 MPa Grade Count:11 |
| Elongation at Break | 4.50 - 5.80 % | 4.50 - 5.80 % | Average value: 4.87 % Grade Count:6 |
| Modulus of Elasticity | 1.52 - 3.38 GPa | 220 - 490 ksi | Average value: 2.46 GPa Grade Count:14 |
| Flexural Yield Strength | 57.0 - 117 MPa | 8270 - 17000 psi | Average value: 97.6 MPa Grade Count:13 |
| Flexural Modulus | 1.86 - 3.38 GPa | 270 - 490 ksi | Average value: 2.76 GPa Grade Count:10 |
| Compressive Yield Strength | 117 - 124 MPa | 17000 - 18000 psi | Average value: 119 MPa Grade Count:3 |
| Izod Impact, Notched | 0.149 - 1.10 J/cm | 0.280 - 2.06 ft-lb/in | Average value: 0.425 J/cm Grade Count:7 |
| 0.200 - 0.500 J/cm @Temperature -18.0 - -18.0 °C | 0.375 - 0.937 ft-lb/in @Temperature -0.400 - -0.400 °F | Average value: 0.275 J/cm Grade Count:4 | |
| Izod Impact, Unnotched | 0.320 - 0.587 J/cm | 0.600 - 1.10 ft-lb/in | Average value: 0.427 J/cm Grade Count:5 |
| Gardner Impact | 0.450 - 5.30 J | 0.332 - 3.91 ft-lb | Average value: 2.49 J Grade Count:4 |
| Falling Dart Impact | 8.13 - 13.6 J | 6.00 - 10.0 ft-lb | Average value: 10.3 J Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Shielding Effectiveness | 40.0 - 120 dB | 40.0 - 120 dB | Average value: 73.8 dB Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.2 - 101 µm/m-°C | 29.0 - 56.0 µin/in-°F | Average value: 75.7 µm/m-°C Grade Count:14 |
| Thermal Conductivity | 0.130 - 0.190 W/m-K | 0.900 - 1.32 BTU-in/hr-ft²-°F | Average value: 0.160 W/m-K Grade Count:4 |
| Maximum Service Temperature, Air | 60.0 - 88.0 °C | 140 - 190 °F | Average value: 74.2 °C Grade Count:8 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 - 98.9 °C | 170 - 210 °F | Average value: 87.7 °C Grade Count:14 |
| Vicat Softening Point | 105 - 115 °C | 221 - 239 °F | Average value: 110 °C Grade Count:4 |
| Minimum Service Temperature, Air | -55.0 - -34.0 °C | -67.0 - -29.2 °F | Average value: -51.5 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.46 - 1.49 | 1.46 - 1.49 | Average value: 1.48 Grade Count:5 |
| Haze | 1.00 - 3.00 % | 1.00 - 3.00 % | Average value: 1.78 % Grade Count:7 |
| Gloss | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:4 |
| Transmission, Visible | 63.0 - 92.0 % | 63.0 - 92.0 % | Average value: 90.3 % Grade Count:10 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 143 - 160 °C | 289 - 320 °F | Average value: 156 °C Grade Count:4 |