- 熔体流动速率 [g/10min]: 27.0
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.16
- 弯曲强度 [MPa]: 64.8
- 弯曲模量 [MPa]: 2.96
- 热变形温度 [℃]: 80.6
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 27 g/10 min @Load 3.80 kg, Temperature 230 °C | 27 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 64.8 MPa | 9400 psi | ASTM D638 |
| Tensile Modulus | 2.90 GPa | 420 ksi | ASTM D638 |
| Flexural Strength | <= 96.5 MPa | <= 14000 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 430 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.187 W/m-K | 1.30 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.6 °C | 177 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | annealed; ASTM D648 |
| Vicat Softening Point | 81.1 °C | 178 °F | 50°C/hr; 50N; ASTM D1525 |
| 87.2 °C | 189 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C | 1.49 @Temperature 73.0 °F | ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm | <= 2.0 % @Thickness 0.125 in | ASTM D1003 |
| Transmission, Visible | 92 % @Thickness 3.17 mm | 92 % @Thickness 0.125 in | ASTM D1003 |