- 熔体流动速率 [g/10min]: 2.0
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.587
- 弯曲强度 [MPa]: 37.9
- 弯曲模量 [MPa]: 1.72
- 热变形温度 [℃]: 88.9
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | weight gain after 24 hr. immersion; ASTM D570 |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 2.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 38 | 38 | ASTM D785 |
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 1.81 GPa | 263 ksi | ASTM D638 |
| Flexural Strength | <= 55.2 MPa | <= 8000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 99.0 µm/m-°C | 55.0 µin/in-°F | ASTM E831 |
| 68.4 µm/m-°C @Temperature -40.0 °C | 38.0 µin/in-°F @Temperature -40.0 °F | ASTM E831 | |
| 82.8 µm/m-°C @Temperature -17.8 °C | 46.0 µin/in-°F @Temperature 0.000 °F | ASTM E831 | |
| 113 µm/m-°C @Temperature 37.8 °C | 63.0 µin/in-°F @Temperature 100 °F | ASTM E831 | |
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | annealed; ASTM D648 |
| Vicat Softening Point | 82.8 °C | 181 °F | 50°C/hr; 50N; ASTM D1525 |
| 93.3 °C | 200 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C | 1.49 @Temperature 73.0 °F | ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm | <= 2.0 % @Thickness 0.125 in | Diffusion; ASTM D1003 |
| Transmission, Visible | 90 % @Thickness 3.17 mm | 90 % @Thickness 0.125 in | ASTM D1003 |