- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.15
- 缺口冲击强度: 0.481
- 弯曲强度 [MPa]: 49.6
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 49.6 MPa | 7190 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Modulus of Elasticity | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7010 psi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Gardner Impact | 3.05 J | 2.25 ft-lb | Falling Weight; ASTM D3029GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate A, ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |