- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.1
- 缺口冲击强度: 0.085
- 拉伸强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 2.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 220 °C | 13 g/10 min @Load 22.0 lb, Temperature 428 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched | 0.0850 J/cm @Temperature 23.0 °C | 0.159 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C @Load 5.10 kg | 199 °F @Load 11.2 lb | 120°C/hr; ISO 306 |
| 102 °C @Load 1.02 kg | 216 °F @Load 2.25 lb | 120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Dry Time | 2.00 - 4.00 hour @Temperature 70.0 °C | 2.00 - 4.00 hour @Temperature 158 °F | |