- 熔体流动速率 [g/10min]: 24.0
- 缺口冲击强度: 0.192
- 弯曲模量 [MPa]: 3.17
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D951 |
| Melt Flow | 24 g/10 min @Load 3.80 kg, Temperature 230 °C | 24 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89 | 89 | ASTM D785 |
| Tensile Strength at Break | 63.4 MPa | 9200 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Elongation at Yield | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Strength | 107 MPa | 15500 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 0.192 J/cm @Diameter 6.35 mm | 0.360 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 100 °C | 40.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C @Thickness 6.35 mm | 180 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Yellow Index | <= 1.0 % | <= 1.0 % | ASTM D1925 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 210 - 243 °C | 410 - 470 °F | Cylinder Temp |
| Melt Temperature | 210 - 243 °C | 410 - 470 °F | |
| Mold Temperature | 32.2 - 79.4 °C | 90.0 - 175 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |