- 熔体流动速率 [g/10min]: 6.3
- 密度 [g/cm3]: 1.17
- 缺口冲击强度: 0.48
- 弯曲强度 [MPa]: 58.0
- 透光率 [%]: 91.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Melt Flow | 6.3 g/10 min | 6.3 g/10 min | Condition 230/3.8; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 4.6 % | 4.6 % | ASTM D638 |
| Modulus of Elasticity | 3.30 GPa | 479 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Gardner Impact | 1.60 J | 1.18 ft-lb | ASTM D3029 GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 91.6 % | 91.6 % | Luminous Transmittance, ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 215 - 249 °C | 419 - 480 °F | |