- 熔体流动速率 [g/10min]: 9.0
- 缺口冲击强度: 0.694
- 弯曲模量 [MPa]: 1.65
- 透光率 [%]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D951 |
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 54 | 54 | ASTM D785 |
| Tensile Strength at Break | 39.3 MPa | 5700 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.14 GPa | 310 ksi | ASTM D638 |
| Flexural Strength | 57.2 MPa | 8300 psi | ASTM D790 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Diameter 6.35 mm | 1.30 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| 0.747 J/cm @Diameter 3.17 mm | 1.40 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 | |
| 0.267 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 0.500 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 95.4 µm/m-°C @Temperature 0.000 - 100 °C | 53.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.35 mm | 194 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.52 | 1.52 | ASTM D542 |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Yellow Index | -0.300 % | -0.300 % | ASTM E313 |
| Transmission, Visible | 85 % | 85 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 193 - 246 °C | 380 - 475 °F | Cylinder Temp |
| Melt Temperature | 204 - 246 °C | 400 - 475 °F | |
| Mold Temperature | 32.2 - 60.0 °C | 90.0 - 140 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |