- 熔体流动速率 [g/10min]: 2.1
- 缺口冲击强度: 1.17
- 弯曲模量 [MPa]: 1.65
- 透光率 [%]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.38 % | <= 0.38 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D951 |
| Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.1 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 33 | 33 | ASTM D785 |
| Tensile Strength at Break | 36.7 MPa | 5320 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 3.9 % | 3.9 % | ASTM D638 |
| Tensile Modulus | 1.72 GPa | 250 ksi | ASTM D638 |
| Flexural Strength | 59.2 MPa | 8590 psi | ASTM D790 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Diameter 6.35 mm | 2.20 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 86.4 µm/m-°C @Temperature 0.000 - 100 °C | 48.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C @Thickness 6.35 mm | 163 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 93.9 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Yellow Index | -1.00 % | -1.00 % | ASTM E313 |
| Transmission, Visible | 85 % | 85 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 218 - 249 °C | 425 - 480 °F | Cylinder Temp |
| Melt Temperature | 216 - 249 °C | 420 - 480 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |