- 熔体流动速率 [g/10min]: 4.2
- 缺口冲击强度: 0.641
- 弯曲模量 [MPa]: 2.76
- 透光率 [%]: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D951 |
| Melt Flow | 4.2 g/10 min @Load 5.00 kg, Temperature 230 °C | 4.2 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 56 | 56 | ASTM D785 |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 3.6 % | 3.6 % | ASTM D638 |
| Tensile Modulus | 2.96 GPa | 430 ksi | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Diameter 6.35 mm | 1.20 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| 0.481 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 0.900 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 100 °C | 40.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C @Thickness 6.35 mm | 189 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.5 % | 2.5 % | ASTM D1003 |
| Yellow Index | -1.00 % | -1.00 % | ASTM E313 |
| Transmission, Visible | 86 % | 86 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 204 - 246 °C | 400 - 475 °F | Cylinder Temp |
| Melt Temperature | 204 - 246 °C | 400 - 475 °F | |
| Mold Temperature | 48.9 - 76.7 °C | 120 - 170 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |