- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.11
- 缺口冲击强度: 0.59
- 断裂伸长率 [%]: 72.0
- 弯曲强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 2.30
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Viscosity | 975000 cP @Shear Rate 100 1/s, Temperature 240 °C | 975000 cP @Shear Rate 100 1/s, Temperature 464 °F | Approximate value |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
| Melt Flow | 2.2 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.2 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Spiral Flow | 46.0 cm | 18.1 in | 215°C |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 39 | 39 | ASTM D785 |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ASTM D638 |
| Elongation at Break | 6.7 % | 6.7 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Compressive Yield Strength | 79.0 MPa | 11500 psi | ASTM D695 |
| Izod Impact, Notched | 0.590 J/cm @Thickness 6.35 mm, Temperature 0.000 °C | 1.11 ft-lb/in @Thickness 0.250 in, Temperature 32.0 °F | bar; ASTM D256 |
| 1.01 J/cm @Diameter 6.35 mm | 1.89 ft-lb/in @Diameter 0.250 in | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 92.5 µm/m-°C @Temperature 0.000 - 100 °C | 51.4 µin/in-°F @Temperature 32.0 - 212 °F | |
| Specific Heat Capacity | 1.30 J/g-°C @Temperature 25.0 °C | 0.311 BTU/lb-°F @Temperature 77.0 °F | |
| 1.90 J/g-°C @Temperature 100 °C | 0.454 BTU/lb-°F @Temperature 212 °F | ||
| 2.30 J/g-°C @Temperature 175 °C | 0.550 BTU/lb-°F @Temperature 347 °F | ||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 19 % | 19 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.515 | 1.515 | ASTM D542 |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Yellow Index | -0.300 % | -0.300 % | |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 216 - 249 °C | 421 - 480 °F | |