- 熔体流动速率 [g/10min]: 3.5
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.267
- 弯曲模量 [MPa]: 2.21
- 透光率 [%]: 91.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Bulk Density | 0.710 g/cc | 0.0257 lb/in³ | ASTM D1895 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 68 | 68 | ASTM D785 |
| Tensile Strength at Break | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.21 GPa | 320 ksi | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 0.000 °C | 0.500 ft-lb/in @Temperature 32.0 °F | 1/4" bar; ASTM D256 |
| 0.454 J/cm @Temperature 23.0 °C | 0.850 ft-lb/in @Temperature 73.4 °F | 1/4" bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 156 °C | 40.0 µin/in-°F @Temperature 32.0 - 312 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C @Thickness 6.35 mm | 196 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 98.9 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Yellow Index | <= 0.30 % | <= 0.30 % | ASTM D1925 |
| Transmission, Visible | 91.5 % | 91.5 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | |
| Mold Temperature | 43.3 - 82.2 °C | 110 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |