- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.11
- 缺口冲击强度: 1.3
- 断裂伸长率 [%]: 62.0
- 弯曲强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 2.00
- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
| Elongation at Break | 8.3 % | 8.3 % | ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Compressive Yield Strength | 56.0 MPa | 8120 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm @Diameter 6.35 mm | 2.44 ft-lb/in @Diameter 0.250 in | bar; ASTM D256 |
| 0.800 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 1.50 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | bar; ASTM D256 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | J/cm; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 83.0 µm/m-°C @Temperature 20.0 °C | 46.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.30 J/g-°C @Temperature 25.0 °C | 0.311 BTU/lb-°F @Temperature 77.0 °F | |
| 1.90 J/g-°C @Temperature 100 °C | 0.454 BTU/lb-°F @Temperature 212 °F | ||
| 2.30 J/g-°C @Temperature 175 °C | 0.550 BTU/lb-°F @Temperature 347 °F | ||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | ASTM D1003 |