- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 0.43
- 断裂伸长率 [%]: 90.0
- 弯曲强度 [MPa]: 61.0
- 弯曲模量 [MPa]: 2.80
- 透光率 [%]: 84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Viscosity | 2.00e+6 cP @Shear Rate 100 1/s, Temperature 240 °C | 2.00e+6 cP @Shear Rate 100 1/s, Temperature 464 °F | Approximate value |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 4.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Spiral Flow | 74.0 cm | 29.1 in | 215°C; 1/4 in half round channel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm @Diameter 6.35 mm | 0.806 ft-lb/in @Diameter 0.250 in | bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.30 J/g-°C @Temperature 25.0 °C | 0.311 BTU/lb-°F @Temperature 77.0 °F | |
| 1.90 J/g-°C @Temperature 100 °C | 0.454 BTU/lb-°F @Temperature 212 °F | ||
| 2.30 J/g-°C @Temperature 175 °C | 0.550 BTU/lb-°F @Temperature 347 °F | ||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Oxygen Index | 17.2 % | 17.2 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.515 | 1.515 | ASTM D542 |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Transmission, Visible | 84 % | 84 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 216 - 249 °C | 421 - 480 °F | |