- 熔体流动速率 [g/10min]: 1.9
- 缺口冲击强度: 5.66
- 拉伸强度 [MPa]: 62.7
- 弯曲模量 [MPa]: 2.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.26 % | <= 0.26 % | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D551 | ||
| Melt Flow | 1.9 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.9 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 55 | 55 | ASTM D785 | ||
| Tensile Strength, Yield | 62.7 MPa | 9090 psi | ASTM D638 | ||
| Elongation at Break | 73 % | 73 % | ASTM D638 | ||
| Elongation at Yield | 4.7 % | 4.7 % | ASTM D638 | ||
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 | ||
| Flexural Strength | 91.7 MPa | 13300 psi | ASTM D790 | ||
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 | ||
| Izod Impact, Notched | 5.66 J/cm @Thickness 6.35 mm, Temperature 22.8 °C | 10.6 ft-lb/in @Thickness 0.250 in, Temperature 73.0 °F | |||
| 8.38 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 15.7 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ||||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 93.6 µm/m-°C @Temperature 0.000 - 100 °C | 52.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | ASTM D648 | ||
| Vicat Softening Point | 152 °C | 306 °F | ASTM D1525 | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Chemical Resistance to Acetone | Non Resistant | Visual Inspection, immersion 24hrs | |||
| Chemical Resistance to Ammonia | Limited Resistance | Elongation Retention, immersion 24hrs | |||
| Limited Resistance | Resistance under Strength Retention | ||||
| Non Resistant | Elongation Retention, immersion 100hrs | ||||
| Resistant | Strength Retention, immersion 100hrs | ||||
| Resistant | Strength Retention, immersion 24hrs | ||||
| Chemical Resistance to Antifreeze | Non Resistant | Strength Retention (3100 psi, 170hrs) | |||
| Chemical Resistance to Baking Soda Paste | Resistant | Visual Inspection, exposed 92hrs | |||
| Chemical Resistance to Bleach 10% | Resistant | Elongation Retention, immersion 24hrs | |||
| Chemical Resistance to Butter | Limited Resistance | Strength Retention (3100 psi, 24hrs) | |||
| Resistant | Stain Resistance, 24hrs | ||||
| Chemical Resistance to Citric Acid Solution (0.1%) | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Coffee | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Diesel Fuel | Limited Resistance | Strength Retention (1750 psi, 70hrs) | |||
| Chemical Resistance to DOP (Phthalate) | Non Resistant | Time to Craze under Stress (4000 psi) | |||
| Chemical Resistance to Ethanol | Limited Resistance | Strength Retention, immersion 1000hrs | |||
| Resistant | Strength Retention, immersion 500hrs | ||||
| Chemical Resistance to Ethylene Glycol | Resistant | Visual Inspection, 1hr immersion | |||
| Chemical Resistance to Fantastic Cleaner | Limited Resistance | Resistance under Strength Retention | |||
| Resistant | Strength Retention, immersion 100hrs | ||||
| Resistant | Strength Retention, immersion 24hrs | ||||
| Resistant | Elongation Retention, immersion 100hrs | ||||
| Resistant | Elongation Retention, immersion 24hrs | ||||
| Chemical Resistance to Fluorides | Resistant | Visual Inspection, exposed 92hrs | |||
| Chemical Resistance to French's Mustard | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Gasoline | Limited Resistance | Strength Retention, immersion 500hrs | |||
| Non Resistant | Strength Retention, immersion 1000hrs | ||||
| Chemical Resistance to Glycerin | Resistant | Visual Inspection, immersion 170hrs, 150F | |||
| Chemical Resistance to Heavy Duty Detergent | Resistant | Visual Inspection, immersion 1000hrs | |||
| Chemical Resistance to Heptane | Resistant | Strength Retention, immersion 1000hrs | |||
| Chemical Resistance to Igepal (1%) Solution | Resistant | Strength Retention (3750 psi, 70hrs) | |||
| Chemical Resistance to IPA | Non Resistant | Strength Retention (3100 psi, 70hrs) | |||
| Resistant | Resistance under Strength Retention | ||||
| Chemical Resistance to IPA/Water 50% | Resistant | Visual Inspection, 1hr immersion | |||
| Chemical Resistance to Kerosene | Resistant | Strength Retention (3100 psi, 10hrs) | |||
| Chemical Resistance to Lipids | Limited Resistance | Strength Retention (3100 psi, 70hrs) | |||
| Resistant | Resistance under Strength Retention | ||||
| Chemical Resistance to Lipstick | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Octane/Toluene 75%/25% | Limited Resistance | Strength Retention, immersion 1000hrs | |||
| Resistant | Strength Retention, immersion 500hrs | ||||
| Chemical Resistance to Rust Inhibitor Veto #4224 | Non Resistant | Strength Retention (3100 psi, 170hrs) | |||
| Chemical Resistance to Rust Inhibitor Veto #53359 | Limited Resistance | Strength Retention (3100 psi, 170hrs) | |||
| Chemical Resistance to Soap and Water | Resistant | Elongation Retention, immersion 100hrs | |||
| Resistant | Elongation Retention, immersion 24hrs | ||||
| Resistant | Resistance under Strength Retention | ||||
| Resistant | Strength Retention, immersion 100hrs | ||||
| Resistant | Strength Retention, immersion 24hrs | ||||
| Chemical Resistance to Sodium Hydroxide (0.5%) | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Tea | Resistant | Stain Resistance, 24hrs | |||
| Chemical Resistance to Toothpaste | Resistant | Visual Inspection, exposed 92hrs | |||
| Chemical Resistance to Transmission Fluid | Resistant | Strength Retention (3100 psi, 170hrs) | |||
| Chemical Resistance to Vinyl Gasket | Resistant | Strength Retention (3100 psi, 24hrs) | |||
| Resistance to Palmolive Dishwasher/Water 50% | Resistant | Visual Inspection, immersion 24hrs | |||