- 熔体流动速率 [g/10min]: 7.9
- 缺口冲击强度: 0.747
- 拉伸强度 [MPa]: 33.64
- 透光率 [%]: 77.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.9 g/10 min @Load 5.00 kg, Temperature 230 °C | 7.9 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 44 | 44 | ASTM D785 |
| Tensile Strength, Yield | 33.64 MPa | 4879 psi | ASTM D638 |
| Elongation at Break | 19 % | 19 % | ASTM D638 |
| Elongation at Yield | 4.7 % | 4.7 % | ASTM D638 |
| Tensile Modulus | 1.53 GPa | 222 ksi | ASTM D638 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | ASTM D256 |
| 0.801 J/cm @Thickness 3.17 mm, Temperature 0.000 °C | 1.50 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F | ASTM D256 | |
| 0.801 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 | |
| 0.801 J/cm @Thickness 6.35 mm, Temperature 0.000 °C | 1.50 ft-lb/in @Thickness 0.250 in, Temperature 32.0 °F | ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.90e+10 ohm-cm | 8.90e+10 ohm-cm | 12% RH; ASTM D257-78 |
| 1.80e+11 ohm-cm | 1.80e+11 ohm-cm | After 24 hours Cold Water Showering; ASTM D257-78 | |
| Surface Resistance | 2.60e+9 ohm | 2.60e+9 ohm | 12% RH; ASTM EOS/ESD 511.11 |
| 2.70e+9 ohm | 2.70e+9 ohm | After 24 hours Cold Water Showering; ASTM FTM 101C | |
| Static Decay | 0.020 sec | 0.020 sec | After 24 hours Cold Water Showering; ASTM EOS/ESD 511.11 |
| 0.030 sec | 0.030 sec | At 23°C, 12% RH; ASTM FTM 101C | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10.2 % | 10.2 % | ASTM D1003 |
| Gloss | 113 % | 113 % | At 60°; ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 - 246 °C | 400 - 475 °F | |
| Mold Temperature | 32.2 - 60.0 °C | 90.0 - 140 °F | |
| Drying Temperature | 82.2 °C | 180 °F | 3-4hrs |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | Hydraulic |
| Back Pressure | <= 0.689 MPa | <= 100 psi | |
| Screw Speed | 20 - 70 rpm | 20 - 70 rpm | 3.5:1 Compression |