- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.11
- 断裂伸长率 [%]: 41.2
- 弯曲模量 [MPa]: 1.373
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 24 hrs.; ASTM D570 |
| Melt Flow | 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 37 | 37 | ASTM D785 |
| Tensile Strength at Break | 32.3 MPa | 4690 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Yield Strength | 41.2 MPa | 5970 psi | ASTM D790 |
| Flexural Modulus | 1.373 GPa | 199.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.11 J/cm | 2.07 ft-lb/in | 0.250 inches; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature 20.0 °C | 66.6 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.46 J/g-°C | 0.349 BTU/lb-°F | |
| Thermal Conductivity | 0.209 W/m-K | 1.45 BTU-in/hr-ft²-°F | ASTM D177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.6 °C | 186 °F | ASTM D648 |
| Vicat Softening Point | 101.0 °C | 213.8 °F | ASTM D1525; 1 kg |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Transmission, Visible | 92 % @Thickness 3.20 mm | 92 % @Thickness 0.126 in | ASTM D1003 |