- 熔体流动速率 [g/10min]: 1.309
- 密度 [g/cm3]: 1.19
- 热变形温度 [℃]: 101.0
- 透光率 [%]: 86.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | ||
| Melt Flow | 1.309 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.309 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 63.0 µm/m-°C @Temperature 0.000 - 50.0 °C | 35.0 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 | ||
| Vicat Softening Point | 105 °C | 221 °F | B50; ISO 306 | ||
| Glass Transition Temp, Tg | 108 °C | 226 °F | IEC 10006 | ||
| Glow Wire Test | 700 °C | 1290 °F | IEC 695-2 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 86 % | 86 % | Transmission Factor; DIN 5036 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | Barrel Temperature | ||
| Die Temperature | 220 - 260 °C | 428 - 500 °F | |||
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |||
| Drying Temperature | <= 95.0 °C | <= 203 °F | Predrying | ||
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier | ||
| Descriptive Properties | |||||
| Energy Half Angle | 14° | IEC 695-2 | |||
| Fire Rating | B2 | DIN 4102 | |||