- 熔体流动速率 [g/10min]: 3.45
- 密度 [g/cm3]: 1.19
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Melt Flow | 3.45 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.45 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 0.000 - 50.0 °C | 44.4 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 |
| Vicat Softening Point | 104 °C | 219 °F | B50; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 707 |
| Glass Temperature Coefficient | 108 | 108 | ISO 11357 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Transmission, Visible | 92 % | 92 % | Transmission Factor; DIN 5036 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | Barrel Temperature |
| Die Temperature | 220 - 260 °C | 428 - 500 °F | |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Drying Temperature | <= 94.0 °C | <= 201 °F | Predrying |
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier |