- 熔体流动速率 [g/10min]: 0.112
- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 1.2
- 拉伸强度 [MPa]: 25.0
- 热变形温度 [℃]: 73.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C, 50%; ISO 62 |
| Water Absorption at Saturation | 1.2 % | 1.2 % | Immersion; ISO 62 |
| Melt Flow | 0.112 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.112 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 0.950 GPa | 138 ksi | 1 mm/min; ISO 527 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 150 µm/m-°C @Temperature 0.000 - 50.0 °C | 83.3 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Vicat Softening Point | 75.0 °C | 167 °F | B50; ISO 306 |
| Glass Transition Temp, Tg | 115 °C | 239 °F | ISO 11357 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 707 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Transmission, Visible | 89 % | 89 % | Transmission Factor; DIN 5036 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 240 °C | 446 - 464 °F | Cylinder/Barrel Temperature |
| Melt Temperature | 230 - 240 °C | 446 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | <= 70.0 °C | <= 158 °F | Predrying |
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier |