- 熔体流动速率 [g/10min]: 9.477
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 1.9
- 拉伸强度 [MPa]: 55.0
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | 23°C, 50%; ISO 62 | ||
| Water Absorption at Saturation | 1.9 % | 1.9 % | Immersion; ISO 62 | ||
| Melt Flow | 9.477 g/10 min @Load 3.80 kg, Temperature 230 °C | 9.477 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | ||
| Elongation at Break | 25 % | 25 % | ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 90.0 µm/m-°C @Temperature 0.000 - 50.0 °C | 50.0 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 | ||
| Vicat Softening Point | 96.0 °C | 205 °F | B50; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 707 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.49 | 1.49 | ISO 489 | ||
| Transmission, Visible | 92 % | 92 % | Transmission Factor; DIN 5036 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | Barrel Temperature | ||
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |||
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |||
| Drying Temperature | <= 85.0 °C | <= 185 °F | Predrying | ||
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier | ||
| Descriptive Properties | |||||
| Fire Rating | B2 | DIN 4102 | |||