- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 1.07
- 断裂伸长率 [%]: 72.0
- 弯曲强度 [MPa]: 40.0
- 硬度: 97.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 - 1.45 g/cc | 0.0488 - 0.0524 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | |
| Modulus of Elasticity | 2.557 GPa | 370.9 ksi | |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Izod Impact, Notched | 1.07 - 2.14 J/cm @Temperature 23.0 °C | 2.00 - 4.01 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | annealed; ASTM D648 |