- 密度 [g/cm3]: 1.46
- 断裂伸长率 [%]: 70.0
- 弯曲强度 [MPa]: 45.0
- 硬度: 98.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 - 1.49 g/cc | 0.0527 - 0.0538 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | |
| Modulus of Elasticity | 2.896 GPa | 420.0 ksi | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
| Impact Test | 7.24 J | 5.34 ft-lb | Dynatup Max Energy |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 163 - 200 °C | 325 - 392 °F | Forming Temperature |