- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 74.0
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 3.099
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 98 % | 98 % | |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 3.099 GPa | 449.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C | 0.599 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 157 - 207 °C | 315 - 405 °F | |
| Melt Temperature | 196 - 207 °C | 385 - 405 °F | |
| Mold Temperature | 32.2 - 60.0 °C | 90.0 - 140 °F | |
| Drying Temperature | 54.4 °C | 130 °F | |
| Dry Time | 4 hour | 4 hour | Usually not needed |