- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 1.07
- 断裂伸长率 [%]: 44.0
- 弯曲强度 [MPa]: 33.0
- 硬度: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 106 % | 106 % | |
| Modulus of Elasticity | 1.868 GPa | 270.9 ksi | |
| Flexural Yield Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Izod Impact, Notched | 1.07 - 1.60 J/cm @Temperature 23.0 °C | 2.00 - 3.00 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 100000 ohm | 100000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | annealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |