- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 8.01
- 断裂伸长率 [%]: 66.0
- 弯曲强度 [MPa]: 42.0
- 硬度: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | |
| Modulus of Elasticity | 2.482 GPa | 360.0 ksi | |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C | 15.0 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.5 °C | 168 °F | annealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness 0.700 - 3.00 mm | 122 °F @Thickness 0.0276 - 0.118 in | |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 0.700 - 3.00 mm | 122 °F @Thickness 0.0276 - 0.118 in | |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 0.700 - 3.00 mm | 122 °F @Thickness 0.0276 - 0.118 in | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 163 - 200 °C | 325 - 392 °F | Forming Temperature |