- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.3
- 缺口冲击强度: 1.6
- 弯曲模量 [MPa]: 3.40
- 热变形温度 [℃]: 100.0
- 透光率 [%]: 74.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 94 | 94 | ISO 2039-2 |
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 73.0 MPa | 10600 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.60 kJ/m² | 0.761 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.140 J/cm² | 0.666 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75A |
| Vicat Softening Point | 102 °C | 216 °F | ISO 306B |
| 109 °C | 228 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Haze | 66 % | 66 % | ASTM D1003 |
| Transmission, Visible | 74 % | 74 % | ASTM D1003 |