- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.4
- 缺口冲击强度: 3.3
- 弯曲模量 [MPa]: 2.50
- 热变形温度 [℃]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ISO 2039-2 |
| Tensile Strength | 37.0 MPa | 5370 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | ISO 527 |
| Flexural Strength | 51.0 MPa | 7400 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.30 kJ/m² | 1.57 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Impact Test | 1.20 J | 0.885 ft-lb | Instrumented Falling Weight Impact; ISO 6603/2 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ISO 75A |
| Vicat Softening Point | 76.0 °C | 169 °F | ISO 306B |
| 89.0 °C | 192 °F | ISO 306A | |