- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.3
- 缺口冲击强度: 4.5
- 弯曲模量 [MPa]: 1.39
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 20 | 20 | ISO 2039-2 |
| Tensile Strength | 38.0 MPa | 5510 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Flexural Modulus | 1.39 GPa | 202 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.420 J/cm² | 2.00 ft-lb/in² | ISO 179/1eA |
| 4.20 J/cm² | 20.0 ft-lb/in² | ISO 179/1eU | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 123 µm/m-°C | 68.3 µin/in-°F | ASTM E831 |
| Vicat Softening Point | 83.0 °C | 181 °F | ISO 306B |
| 94.0 °C | 201 °F | ISO 306A | |
| Heat Distortion Temperature | 80.0 °C | 176 °F | ISO 75A |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |