- 熔体流动速率 [g/10min]: 5.5
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 2.00
- 硬度: 61.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.5 g/10 min @Load 11.0 lb, Temperature 392 °F | Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 61 | 61 | ASTM D785 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 52 % | 52 % | ASTM D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Strength | 46.0 MPa | 6670 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | reverse notched; ASTM D256 |
| Izod Impact, Unnotched | 2.20 J/cm | 4.12 ft-lb/in | ASTM D256 |
| Gardner Impact | 1.70 J | 1.25 ft-lb | Geometry GB; ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.56 | 1.56 | nD; ASTM D542 |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 179 - 213 °C | 354 - 415 °F | |
| Middle Barrel Temperature | 185 - 218 °C | 365 - 424 °F | |
| Front Barrel Temperature | 191 - 224 °C | 376 - 435 °F | |
| Melt Temperature | 204 - 238 °C | 399 - 460 °F | |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Back Pressure | 0.689 MPa | 100 psi | |