Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer

Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer 物性表: Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer物性表及特性介绍,Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer注塑参数详情,如需Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 4.0
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 0.25
  • 弯曲强度 [MPa]: 43.0
  • 弯曲模量 [MPa]: 2.50
  • 硬度: 86.0
  • 透光率 [%]: 89.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.05 g/cc1.05 g/ccASTM D792
Water Absorption 0.10 %0.10 %24 hr.; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm0.0020 - 0.0060 in/inASTM D955
Melt Flow 4.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C
4.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 8686ASTM D785
Tensile Strength, Ultimate 43.0 MPa6240 psiASTM D638
Elongation at Break 20 %20 %ASTM D638
Tensile Modulus 2.50 GPa363 ksiASTM D638
Flexural Strength 68.0 MPa9860 psiASTM D790
Flexural Modulus 2.50 GPa363 ksiASTM D790
Izod Impact, Notched 0.250 J/cm0.468 ft-lb/inASTM D256
Izod Impact, Unnotched 2.00 J/cm3.75 ft-lb/inASTM D256
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C194 °FASTM D648
Vicat Softening Point 103 °C217 °FASTM D1525
Flammability, UL94 HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
all colors
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.561.56ASTM D542
Haze 1.6 %1.6 %ASTM D1003
Transmission, Visible 89 %89 %ASTM D1003
 
Processing PropertiesMetricEnglishComments
Processing Temperature <= 250 °C<= 482 °F
Rear Barrel Temperature 179 - 213 °C354 - 415 °F
Middle Barrel Temperature 185 - 218 °C365 - 424 °F
Front Barrel Temperature 191 - 224 °C376 - 435 °F
Melt Temperature 204 - 238 °C399 - 460 °F
Mold Temperature 27.0 - 54.0 °C80.6 - 129 °F
Back Pressure 0.689 MPa100 psi
 
Descriptive Properties
Injection Speedmoderate-fast
Pre-Dry Requirements2 hrs. at 65°C

**
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.

Users of our Advanced Search (registration required) may exclude discontinued materials from search results.

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-30407.html

免责声明: 本文 Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4