Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced

Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced 物性表: Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced物性表及特性介绍,Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced注塑参数详情,如需Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.36
  • 弯曲模量 [MPa]: 8.80
  • 热变形温度 [℃]: 210.0
 
Physical PropertiesMetricEnglishComments
Density 1.36 g/cc0.0491 lb/in³ISO 1183
Filler Content 30 %30 %±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm0.0030 in/inWith Flow; ISO 2577
 0.0090 cm/cm0.0090 in/inAcross Flow; ISO 2577
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 80
@Time 15.0 sec
80
@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break <= 160 MPa<= 23200 psiISO/R527
Elongation at Yield 3.0 %3.0 %ISO/R527
Flexural Strength <= 230 MPa<= 33400 psiISO 178
Flexural Modulus 8.80 GPa
@Temperature 23.0 °C
1280 ksi
@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 1.00 J/cm²
@Temperature 23.0 °C
4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C410 °F120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °F120°C/h; ISO 75/1
Vicat Softening Point 215 °C
@Load 5.001 kg
419 °F
@Load 11.03 lb
50°C/h; ISO 306
Flammability, UL94 HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
Glow Wire Test 650 °C
@Thickness 2.00 mm
1200 °F
@Thickness 0.0787 in
IEC 695-2-1

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-30492.html

免责声明: 本文 Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4