- 熔体流动速率 [g/10min]: 3.0
- 缺口冲击强度: 0.441
- 拉伸强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 1.96
- 硬度: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C | 7.0 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 72.6 MPa | 10500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm @Thickness 6.35 mm | 0.827 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 0.490 J/cm @Thickness 3.17 mm | 0.918 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm | 172 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 93.0 °C | 199 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |