- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.534
- 断裂伸长率 [%]: 41.4
- 弯曲强度 [MPa]: 26.2
- 弯曲模量 [MPa]: 2.41
- 热变形温度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 - 1.21 g/cc | 0.0379 - 0.0437 lb/in³ | Average value: 1.13 g/cc Grade Count:5 |
| Filler Content | 10.0 - 20.0 % | 10.0 - 20.0 % | Average value: 17.5 % Grade Count:4 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00400 - 0.00700 cm/cm | 0.00400 - 0.00700 in/in | Average value: 0.00500 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | Average value: 0.00660 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 26.2 - 44.8 MPa | 3800 - 6500 psi | Average value: 41.1 MPa Grade Count:5 |
| Elongation at Break | 2.00 - 8.00 % | 2.00 - 8.00 % | Average value: 4.00 % Grade Count:5 |
| Modulus of Elasticity | 2.76 - 5.52 GPa | 400 - 800 ksi | Average value: 4.21 GPa Grade Count:5 |
| Flexural Yield Strength | 41.4 - 68.9 MPa | 6000 - 10000 psi | Average value: 58.6 MPa Grade Count:5 |
| Flexural Modulus | 2.41 - 4.14 GPa | 350 - 600 ksi | Average value: 3.35 GPa Grade Count:5 |
| Izod Impact, Notched | 0.534 - 1.07 J/cm | 1.00 - 2.00 ft-lb/in | Average value: 0.641 J/cm Grade Count:5 |
| Izod Impact, Unnotched | 2.67 - 5.34 J/cm | 5.00 - 10.0 ft-lb/in | Average value: 3.63 J/cm Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 - 149 °C | 250 - 300 °F | Average value: 141 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 - 138 °C | 230 - 280 °F | Average value: 131 °C Grade Count:5 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 227 °C | 380 - 440 °F | Average value: 210 °C Grade Count:5 |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | Average value: 48.9 °C Grade Count:5 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:5 |