- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.9
- 拉伸强度 [MPa]: 34.5
- 弯曲模量 [MPa]: 1.25
- 热变形温度 [℃]: 93.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | D-1505 | ||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 446 °F | D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | 2 in/min; D-638 | ||
| Elongation at Yield | 10 % | 10 % | 2 in/min; D-638 | ||
| Flexural Modulus | 1.25 GPa | 182 ksi | D-790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | D-648 | ||
| Descriptive Properties | |||||
| process | Fiber | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||