- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.906
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 37.2
- 弯曲模量 [MPa]: 1.53
- 硬度: 101.0
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.906 g/cc | 0.0327 lb/in³ | ASTM D1505 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | ASTM D-570 | ||
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D-955 | ||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 101 | 101 | ASTM D-785 | ||
| Tensile Strength, Yield | 37.2 MPa | 5400 psi | 2 in/min (50 mm/min); ASTM D-638 | ||
| Elongation at Break | 78 % | 78 % | 2 in/min (50 mm/min); ASTM D-638 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 2 in/min (20 mm/min); ASTM D-638 | ||
| Flexural Modulus | 1.53 GPa | 222 ksi | Secant @ 1% strain; ASTM D-790 | ||
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 - 260 °C | 424 - 500 °F | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||