- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 0.955
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.20
- 热变形温度 [℃]: 77.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 200 MPa | 29000 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 33.0 MPa | 4790 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.8 °C | 118 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | UL File #E99379 |