- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 6.73
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.800
- 硬度: 60.0
- 热变形温度 [℃]: 62.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 0.800 GPa | 116 ksi | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Izod Impact, Notched | 6.73 J/cm | 12.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | |