- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.01
- 缺口冲击强度: 0.272
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.900
- 硬度: 100.0
- 热变形温度 [℃]: 91.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Yield | 35 % | 35 % | ASTM D638 |
| Tensile Modulus | 1.900 GPa | 275.5 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.900 GPa | 275.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.272 J/cm | 0.510 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | UL File #E99379 |