- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 2.62
- 拉伸强度 [MPa]: 66.0
- 弯曲模量 [MPa]: 6.498
- 硬度: 110.0
- 热变形温度 [℃]: 162.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 6.498 GPa | 942.5 ksi | ASTM D790 |
| Izod Impact, Notched | 2.62 J/cm | 4.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | |