- 熔体流动速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.961
- 缺口冲击强度: 0.352
- 拉伸强度 [MPa]: 33.0
- 弯曲模量 [MPa]: 1.40
- 硬度: 94.0
- 热变形温度 [℃]: 102.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.500 GPa | 217.5 ksi | ASTM D638 |
| Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C | 136 °F | |