- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.1
- 缺口冲击强度: 1.66
- 拉伸强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 4.149
- 硬度: 92.0
- 热变形温度 [℃]: 157.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.250 GPa | 326.3 ksi | ASTM D638 |
| Flexural Strength | 75.98 MPa | 11020 psi | ASTM D790 |
| Flexural Modulus | 4.149 GPa | 601.8 ksi | ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm | 3.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | |