- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.03
- 缺口冲击强度: 0.587
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 2.299
- 硬度: 65.0
- 热变形温度 [℃]: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 65 | 65 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 17 % | 17 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.299 GPa | 333.5 ksi | ASTM D638 |
| Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
| Flexural Modulus | 2.299 GPa | 333.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |