- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.02
- 缺口冲击强度: 0.422
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 2.60
- 硬度: 74.0
- 热变形温度 [℃]: 123.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 74 | 74 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM D638 |
| Flexural Strength | 46.0 MPa | 6670 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm | 0.790 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |