- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.231
- 缺口冲击强度: 0.299
- 拉伸强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 4.300
- 硬度: 75.0
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.231 g/cc | 0.04447 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | ASTM D790 |
| Flexural Modulus | 4.300 GPa | 623.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | |